1、Int J Adv Manuf Technol(2002)19:253259 2002 Springer-Verlag London LimitedAn Analysis of Draw-Wall Wrinkling in a Stamping Die DesignF.-K.Chen and Y.-C.LiaoDepartment of Mechanical Engineering,National Taiwan University,Taipei,TaiwanWrinkling that occurs in the stamping of tapered square cupsand ste

2、pped rectangular cups is investigated.A commoncharacteristic of these two types of wrinkling is that thewrinkles are found at the draw wall that is relatively unsup-ported.In the stamping of a tapered square cup,the effect ofprocess parameters,such as the die gap and blank-holderforce,on the occurre

3、nce of wrinkling is examined using finite-element simulations.The simulation results show that the largerthe die gap,the more severe is the wrinkling,and suchwrinkling cannot be suppressed by increasing the blank-holderforce.In the analysis of wrinkling that occurred in the stampingof a stepped rect

4、angular cup,an actual production part thathas a similar type of geometry was examined.The wrinklesfound at the draw wall are attributed to the unbalancedstretching of the sheet metal between the punch head and thestep edge.An optimum die design for the purpose of eliminatingthe wrinkles is determine

5、d using finite-element analysis.Thegood agreement between the simulation results and thoseobserved in the wrinkle-free production part validates theaccuracy of the finite-element analysis,and demonstrates theadvantage of using finite-element analysis for stamping diedesign.Keywords:Draw-wall wrinkle

6、;Stamping die;Stepped rec-tangular cup;Tapered square cups1.IntroductionWrinkling is one of the major defects that occur in the sheetmetal forming process.For both functional and visual reasons,wrinkles are usually not acceptable in a finished part.Thereare three types of wrinkle which frequently oc

7、cur in the sheetmetal forming process:flange wrinkling,wall wrinkling,andelastic buckling of the undeformed area owing to residualelastic compressive stresses.In the forming operation of stamp-ing a complex shape,draw-wall wrinkling means the occurrenceCorrespondence and offprint requests to:Profess

8、or F.-K.Chen,Depart-ment of Mechanical Engineering,National Taiwan University,No.1Roosevelt Road,Sec.4,Taipei,Taiwan 10617.E-mail:fkchen?w3.me.ntu.edu.twof wrinkles in the die cavity.Since the sheet metal in the wallarea is relatively unsupported by the tool,the elimination ofwall wrinkles is more d

9、ifficult than the suppression of flangewrinkles.It is well known that additional stretching of thematerial in the unsupported wall area may prevent wrinkling,and this can be achieved in practice by increasing the blank-holder force;but the application of excessive tensile stressesleads to failure by

10、 tearing.Hence,the blank-holder force mustlie within a narrow range,above that necessary to suppresswrinkles on the one hand,and below that which producesfracture on the other.This narrow range of blank-holder forceis difficult to determine.For wrinkles occurring in the centralarea of a stamped part

11、 with a complex shape,a workablerange of blank-holder force does not even exist.In order to examine the mechanics of the formation ofwrinkles,Yoshida et al.1 developed a test in which a thinplate was non-uniformly stretched along one of its diagonals.They also proposed an approximate theoretical mod

12、el in whichthe onset of wrinkling is due to elastic buckling resulting fromthe compressive lateral stresses developed in the non-uniformstress field.Yu et al.2,3 investigated the wrinkling problemboth experimentally and analytically.They found that wrinklingcould occur having two circumferential wav

13、es according totheir theoretical analysis,whereas the experimental results indi-cated four to six wrinkles.Narayanasamy and Sowerby 4examined the wrinkling of sheet metal when drawing it througha conical die using flat-bottomed and hemispherical-endedpunches.They also attempted to rank the propertie

14、s thatappeared to suppress wrinkling.These efforts are focused on the wrinkling problems associa-ted with the forming operations of simple shapes only,suchas a circular cup.In the early 1990s,the successful applicationof the 3D dynamic/explicit finite-element method to the sheet-metal forming proces

15、s made it possible to analyse the wrinklingproblem involved in stamping complex shapes.In the presentstudy,the 3D finite-element method was employed to analysethe effects of the process parameters on the metal flow causingwrinkles at the draw wall in the stamping of a tapered squarecup,and of a step

16、ped rectangular part.A tapered square cup,as shown in Fig.1(a),has an inclineddraw wall on each side of the cup,similar to that existing ina conical cup.During the stamping process,the sheet metalon the draw wall is relatively unsupported,and is therefore254F.-K.Chen and Y.-C.LiaoFig.1.Sketches of(a)a tapered square cup and(b)a steppedrectangular cup.prone to wrinkling.In the present study,the effect of variousprocess parameters on the wrinkling was investigated.In thecase of a stepped rectangul